Properties and structure of RE-Ni-W-P-SiC composite
coating prepared by impulse electrodeposition
SONG Yue-hai(宋曰海), WEI Gang(魏 刚), XIONG Rong-chun(熊蓉春)

College of Materials Science and Engineering, Beijing University of Chemical Technology, Beijing 100029, China

Abstract:The properties and structure of electrodeposited RE (CeO2)-Ni-W-P-SiC composite coating were investigated. The results show that the hardness and electrodepositing speed of composite coatings obtained at an impulse current are higher than those at a direct current. The hardness and wear resistance of the coating are obviously increased by adding RE and SiC. The hardness of the coating increases with the increase of treatment temperature and current density, and reaches the optimum value at 400 ℃ and at 10 A/dm2, respectively. The optimum operation parameters of electrodeposition of the composite coating are as follows: pH value is 4.5, bath temperature is 65 ℃, and current density is 10 A/dm2.

 

Key words: composite coating; impulse current; electrodeposition; hardness

ISSN 1672-7029
CN 43-1423/U

主管:中华人民共和国教育部 主办:中南大学 中国铁道学会 承办:中南大学
湘ICP备09001153号 版权所有:《铁道科学与工程学报》编辑部
------------------------------------------------------------------------------------------
地 址:湖南省长沙市韶山南路22号 邮编:410075
电 话:0731-82655133,82656174   传真:0731-82655133   电子邮箱:jrse@mail.csu.edu.cn