Effects of magnesium content on phase constituents of Al-Mg-Si-Cu alloys
LIU Hong(刘 宏)1, ZHAO Gang(赵 刚)2, LIU Chun-ming(刘春明)2, ZUO Liang(左 良)2

1. School of Mechanical Engineering, Shandong Institute of Light Industry, Ji’nan 250100, China;
2. School of Materials and Metallurgy, Northeastern University, Shenyang 110004, China

Abstract: By means of scanning electron microscopy(SEM), energy dispersive spectrum(EDS), X-ray diffractometry(XRD) and metallographic analysis, the effects of variation of magnesium content on phase constituents of Al-Mg-Si-Cu alloys were investigated. The results indicate that the constituents formed during casting alloys are main Al1.9CuMg4.1Si3.3,Al4(MnFe)3Si2 and Mg2Si, while pure Si is only present in the alloy containing lower magnesium content. Increasing Mg content leads to increasing the amount of Mg2Si, but decreasing the amount of Al1.9CuMg4.1Si3.3 and Al4(MnFe)3Si2. During the following homogenization process, Al1.9CuMg4.1Si3.3 is completely dissolved, Al4(MnFe)3Si2 and pure Si remain unchanged. After rolling and final heat treatment, the constituents in the alloys change no longer.

 

Key words: Al-Mg-Si-Cu alloys; phase constituent; magnesium content; Al1.9CuMg4.1Si3.3; Al4(MnFe)3Si2; Mg2Si

ISSN 1672-7029
CN 43-1423/U

主管:中华人民共和国教育部 主办:中南大学 中国铁道学会 承办:中南大学
湘ICP备09001153号 版权所有:《铁道科学与工程学报》编辑部
------------------------------------------------------------------------------------------
地 址:湖南省长沙市韶山南路22号 邮编:410075
电 话:0731-82655133,82656174   传真:0731-82655133   电子邮箱:jrse@mail.csu.edu.cn