Crystallization behavior of
Ti61.67Zr17.15Ni14.80Cu6.38glass-forming alloy
FAN Jin-duo(范金铎)1, GAO Yi-qun(高逸群)2, LI Shi-zeng(黎仕增)3

1. Beijing General Research Institute for Non-ferrous Metals, Beijing 100088, China;
2. Institute of Precious Metals, Kunming 650221, China;
3. Guangxi Institute of Mechanical & Electrical Technology, Nanning 530007, China

Abstract:Ti61.67Zr17.15Ni14.80Cu6.38(atom fraction, %) metallic glass has applications in brazing. Using the hammer-and-anvil technique, Ti61.67Zr17.15Ni14.80Cu6.38metallic glass was prepared. The crystallization behavior for this metallic glass was investigated by differential scanning calorimetry(DSC), X-ray diffractometry(XRD) and transmission electron microscopy(TEM). There are three stages in DSC curves of crystallization. The reduced glass temperatureTrgis 0.42. The kinetic parameters of crystallization were calculated by a set of equations of the maximum crystallization rate. The crystalline phase formed in the MSI(Metastable stage I) is Zr2Cu, in the MSII isα-Ti and in the MSIII is Ti2Ni. This kind of alloy has lower glass forming ability, and the Ti61.67Zr17.15Ni14.80Cu6.38metallic glass has lower thermal stability.

 

Key words: Ti61.67Zr17.15Ni14.80Cu6.38metallic glass; crystallization behavior; glass forming ability; brazing

ISSN 1672-7029
CN 43-1423/U

主管:中华人民共和国教育部 主办:中南大学 中国铁道学会 承办:中南大学
湘ICP备09001153号 版权所有:《铁道科学与工程学报》编辑部
------------------------------------------------------------------------------------------
地 址:湖南省长沙市韶山南路22号 邮编:410075
电 话:0731-82655133,82656174   传真:0731-82655133   电子邮箱:jrse@mail.csu.edu.cn