Effect of bonding parameters on microstructure and properties of Si3N4/Si3N4 joint brazed by Cu-Zn-Ti filler alloy
ZHANG Jie(张 杰)1, Naka Massaki2, ZHOU Yu(周 玉)1

1. School of Materials Science and Engineering, Harbin Institute of Technology, Harbin 150001, China;
 2. Joining and Welding Research Institute, Osaka University, Ibaraki, 
Osaka 567-0047, Japan

Abstract:Si3N4 ceramic was jointed to Si3N4 ceramic using a filler alloy of Cu-Zn-Ti at 1123-1323K for 0.3-2.7ks. Ti content in the Cu-Zn-Ti filler alloy was 15%(molar fraction). The effect of bonding parameters on the microstructure and mechanical properties of the Si3N4/Si3N4 joint were investigated. The results indicate that with increasing brazing temperature from 1123K to 1323K and brazing time from 0.3ks to 2.7ks, the thickness of the interfacial reaction layer between the filler alloy and the Si3N4 ceramic and the size and amount of the reactant products in the filler alloy increase, leading to an increase in shear strength of the joint from 163 MPa to 276 MPa. It is also found that the fracture behavior of the Si3N4/Si3N4 joint greatly depends on the microstructure of the joint.

 

Key words: Si3N4 ceramic;Cu-Zn-Ti filler alloy;bonding parameters; microstructure; mechanical property

ISSN 1672-7029
CN 43-1423/U

主管:中华人民共和国教育部 主办:中南大学 中国铁道学会 承办:中南大学
湘ICP备09001153号 版权所有:《铁道科学与工程学报》编辑部
------------------------------------------------------------------------------------------
地 址:湖南省长沙市韶山南路22号 邮编:410075
电 话:0731-82655133,82656174   传真:0731-82655133   电子邮箱:jrse@mail.csu.edu.cn