Preparation and properties of continuous Al-containing silicon carbide fibers
YU Yu-xi(余煜玺), LI Xiao-dong(李效东), CAO Feng(曹 峰), 
WANG Ying-de(王应德), ZOU Zhi-chun(邹治春), WANG Jun(王 军), 
ZHENG Chun-man(郑春满), ZHAO Da-fang(赵大方) 

Key Lab of Ceramic Fibers and Composites,  Institute of Aerospace and Materials Engineering, National University of Defence Technology, Changsha 410073, China

Abstract:Continuous SiC(OAl) fibers, named KD-A fibers, were prepared by the melt-spinning of ceramic precursor polyaluminocarbosilane, air-curing, and pyrolizing at 1300℃. These fibers contained small amount of aluminum and 7%-9% oxygen. The KD-A fibers were converted into sintered SiC(Al) fibers, named KD-SA, by sintering at 1800℃. The fibers were characterized by chemical analysis, tensile strength test, SEM and XRD. The tensile strength, elastic modulus and diameter of the KD-A fibers are 2.6GPa, 210GPa, 12-14μm, respectively. The KD-A fibers have higher thermal stability, more excellent oxidation resistance than the Nicalon fibers. The properties of the KD-A fibers have reached the level of Hi-Nicalon fibers. The tensile strength, elastic modulus and diameter of the KD-A fibers are 2.1GPa, 405GPa, 10-12μm, respectively. The KD-SA fibers with nearly stoichiometric component have stable performance at high temperature, and better creep resistance than the Tyranno SA fibers.

 

Key words: continuous silicon carbide fibers; polyaluminocarbosilane; polymer pyrolysis

ISSN 1672-7029
CN 43-1423/U

主管:中华人民共和国教育部 主办:中南大学 中国铁道学会 承办:中南大学
湘ICP备09001153号 版权所有:《铁道科学与工程学报》编辑部
------------------------------------------------------------------------------------------
地 址:湖南省长沙市韶山南路22号 邮编:410075
电 话:0731-82655133,82656174   传真:0731-82655133   电子邮箱:jrse@mail.csu.edu.cn