Preparation and magnetic properties of nanosized (La0.47Gd0.2)Sr0.33MnO3
WANG Gui(王 贵)1, 2, WANG Zheng-de(王正德)2, ZHANG Li-de(张立德)2

1. College of Engineering, Zhanjiang Ocean University, Zhanjiang 524088, China; 
2. Institute of Solid State Physics, Chinese Academy of Sciences, 
Hefei 230031, China

Abstract:Nanosized (La0.47Gd0.2)Sr0.33MnO3 perovskite oxides were prepared at relatively low calcinating temperature of 600℃ and 800℃ for 10h using amorphous complex precursor. Curie temperature(Tc) and magnetocaloric effects(MCE) were investigated. X-ray diffraction(XRD) and electron diffraction(ED) reveal that the resulting products are of pure single-phase rhombohedral perovskite structure. Transmission electron microscopy(TEM) observation finds that the particle sizes are about 40-50nm and 80-100nm, and the Tc are 285.1K and 285.9K, MCE are about 2.02J/(kg•K-1) and 3.90J/(kg•K-1) at 5T magnetic field. A relatively large MCE with a broad peak around Curie temperature is observed in sample sintered at 800℃ for 10h. This suggests that nanosized (La0.47Gd0.2)Sr0.33MnO3 is a suitable material as working substance in magnetic refrigeration in room temperature.

 

Key words: chemical synthesis; nanostructure materials; magnetocaloric effect; magnetic entropy change; perovskite manganite

ISSN 1672-7029
CN 43-1423/U

主管:中华人民共和国教育部 主办:中南大学 中国铁道学会 承办:中南大学
湘ICP备09001153号 版权所有:《铁道科学与工程学报》编辑部
------------------------------------------------------------------------------------------
地 址:湖南省长沙市韶山南路22号 邮编:410075
电 话:0731-82655133,82656174   传真:0731-82655133   电子邮箱:jrse@mail.csu.edu.cn