High temperature performance of arc-sprayed aluminum bronze coatings for steel
ZHANG Zhong-li(张忠礼)1, LI De-yuan(李德元)1, WANG Shui-yong(王水勇)2

1. School of Materials Science and Engineering, Shenyang University of Technology,
Shenyang 110023, China;
2. State Key Laboratory for Corrosion and Protection, Institute of Metal Reseach,
Shenyang 110015, China

Abstract: The high-temperature oxidation behavior of arc-sprayed aluminum bronze coatings on steel substrate was studied during isothermal exposures in air at 900 ℃. The surface morphologies and interface of the coatings after isothermal oxidation at 900 ℃ for different times were observed. The experiments showed that the coatings on steel substrate were not deteriorated and the substrate was protected well, being exposed to high temperatures up to 900 ℃. The coatings withstood more than ten times thermal shock tests without any coating separation. The thermal expansion coefficient of the coatings was measured, revealing not much difference between it and that of steel substrate. After exposure at high temperature, the coatings were still adhered to steel substrate well. Isothermal mass gain of the coatings at elevated temperature in dry air was measured by means of a thermal balance and the oxidation behavior was evaluated by oxidation kinetic curves, exhibiting the oxidation kinetics curve accorded with a parabolic law. The parabolic rate constant of the oxidation kinetic curve is 1.02×10−9 g2∙cm−4∙s−1 for the first 60 min and from 150 min to 2 880 min the constant is 5.1×10−12 g2∙cm−4∙s−1.

 

Key words: aluminum bronze; coatings; arc spray; high temperature oxidation

ISSN 1672-7029
CN 43-1423/U

主管:中华人民共和国教育部 主办:中南大学 中国铁道学会 承办:中南大学
湘ICP备09001153号 版权所有:《铁道科学与工程学报》编辑部
------------------------------------------------------------------------------------------
地 址:湖南省长沙市韶山南路22号 邮编:410075
电 话:0731-82655133,82656174   传真:0731-82655133   电子邮箱:jrse@mail.csu.edu.cn