Initial atmospheric corrosion of zinc in presence of Na2SO4 and (NH4)2SO4
QU Qing(屈 庆)1, LI Lei(李 蕾)1, BAI Wei(白 玮)2, YAN Chuan-wei(严川伟)3

1. Department of Chemistry, Yunnan University, Kunming 650091, China;
2. Department of Chemistry, Yunnan Nationalities University, Kunming 650092, China;
3. Stake Key Laboratory for Corrosion and Protection, Institute of Metal Research,
Chinese Academy of Sciences, Shenyang 110016, China

Abstract: Initial atmospheric corrosion of zinc in the presence of Na2SO4 and (NH4)2SO4 was investigated via quartz crystal microbalance(QCM) in laboratory at relative humidity(RH) of 80% and 25 ℃. The results show that both Na2SO4 and (NH4)2SO4 can accelerate the initial atmospheric corrosion of zinc. The combined effect of Na2SO4 and (NH4)2SO4 on the corrosion of zinc is greater than that caused by (NH4)2SO4 and less than that caused by Na2SO4. Fourier transform infrared spectroscopy(FTIR), X-ray diffractometry(XRD) and scanning electron microscopy(SEM) were used to characterize the corrosion products of zinc. (NH4)2Zn(SO4)2, Zn4SO4(OH)6•5H2O and ZnO present on zinc surface in the presence of (NH4)2SO4 while Zn4SO4(OH)6•5H2O and ZnO are the dominant corrosion products on Na2SO4-treated zinc surface. Probable mechanisms are presented to explain the experimental results.

 

Key words: zinc; Na2SO4; (NH4)2SO4; atmospheric corrosion

ISSN 1672-7029
CN 43-1423/U

主管:中华人民共和国教育部 主办:中南大学 中国铁道学会 承办:中南大学
湘ICP备09001153号 版权所有:《铁道科学与工程学报》编辑部
------------------------------------------------------------------------------------------
地 址:湖南省长沙市韶山南路22号 邮编:410075
电 话:0731-82655133,82656174   传真:0731-82655133   电子邮箱:jrse@mail.csu.edu.cn