TiC/AZ91D composites fabricated by in situ reactive infiltration process and its tensile deformation
WANG Ji-jie(王继杰)1, GUO Jin-hua(郭金花)2, CHEN Li-qing(陈礼清)3

1. Department of Materials Engineering,
Shenyang Institute of Aeronautical Industrial Engineering, Shenyang 110034, China;
2. School of Materials and Metallurgy, Northeastern University, Shenyang 110004, China;
3. Institute of Metal Research, Chinese Academy of Sciences, Shenyang 110016, China

Abstract: An innovative processing route was adopted to fabricate 42.1%(volume fraction) TiC/AZ91D magnesium matrix composites. The reinforcement TiC was in situ synthesized from elemental powders of Ti and C and the matrix magnesium alloy AZ91D pressurelessly infiltrated into the preform of Ti and C. A comparative tensile deformation tests were conducted on the as-synthesized TiC/AZ91D composites and magnesium alloy AZ91D. The true strain—stress curves were fitted by Hollomon relation and their failure mechanisms were finally analyzed. The results show that the in situ formed TiC can increase the tensile strength, and is especially effective at elevated temperatures. Theoretical calculation of the strain hardening exponent (n) for TiC/AZ91D composites indicates that the n value ranges from 0.71 to 0.82 wh, en tensile deformation was carried out at 423−723 K and shows fracture with brittle characteristic. However, the n value of 0.11−0.32 obtained for the matrix alloy AZ91D shows typical ductile features at elevated temperatures.

 

Key words: magnesium-matrix composites; TiC/AZ91D; in situ reactive infiltration; tensile deformation; strain hardening; fracture mechanism

ISSN 1672-7029
CN 43-1423/U

主管:中华人民共和国教育部 主办:中南大学 中国铁道学会 承办:中南大学
湘ICP备09001153号 版权所有:《铁道科学与工程学报》编辑部
------------------------------------------------------------------------------------------
地 址:湖南省长沙市韶山南路22号 邮编:410075
电 话:0731-82655133,82656174   传真:0731-82655133   电子邮箱:jrse@mail.csu.edu.cn