Preparation of TiAl3-Al composite coating by cold spraying
SHEN Li(沈 莉), KONG Ling-yan(孔令艳), XIONG Tian-ying(熊天英), DU Hao(杜 昊), LI Tie-fan(李铁藩)

State Key Laboratory of Corrosion and Protection, Institute of Metal Research, Chinese Academy of Science,
Shenyang 110016, China

Abstract:TiAl3-Al coating was deposited on orthorhombic Ti2AlNb alloy substrate by cold spraying with the mixture of pure Al and Ti as the feedstock powder at a fixed molar ratio of 3׃1 when the spraying distance, gas temperature and gas pressure for the process were 10 mm, 250 ℃ and 1.8 MPa, respectively. The as-sprayed coating was then subjected to heat treatment at 630 ℃ in argon atmosphere for 5 h at a heating rate of 3 ℃/min and an argon gas flow rate of 40 mL/min. The obtained TiAl3-Al composite coating is about 212 μm with a density of 3.16 g/cm3 and a porosity of 14.69% in general. The microhardness and bonding strength for the composite coating are HV525 and 27.12 MPa.

 

Key words: cold spraying; TiAl3-Al composite coating; orthorhombic Ti2AlNb alloy; high temperature oxidation

ISSN 1672-7029
CN 43-1423/U

主管:中华人民共和国教育部 主办:中南大学 中国铁道学会 承办:中南大学
湘ICP备09001153号 版权所有:《铁道科学与工程学报》编辑部
------------------------------------------------------------------------------------------
地 址:湖南省长沙市韶山南路22号 邮编:410075
电 话:0731-82655133,82656174   传真:0731-82655133   电子邮箱:jrse@mail.csu.edu.cn