Fabrication of two-layer flexible copper clad laminate by electroless-Cu plating on surface modified polyimide
Soo-Min HWANG, Jun-Hyung LIM, Chang-Min LEE, Eui-Cheol PARK,
Jun-Hyuk CHOI, Jinho JOO, Hoo-Jeong LEE, Seung-Boo JUNG

School of Advanced Materials Science and Engineering, Sungkyunkwan University, Suwon, Gyeonggi, Korea

Abstract:A flexible copper clad laminate(FCCL) was fabricated using electroless- and electro-Cu plating processes and the effects of pre-treatment time on the adhesion strength of the FCCL were evaluated based on interfacial morphology. The neutralization and catalyst time were varied in the range of 0−20 min and 0.1−10 min, respectively, and the interfacial condition of the FCCL was characterized by atomic force microscopy(AFM) and X-ray photoelectron spectroscopy(XPS). It is observed that the peel strength increases significantly as the neutralization and catalyst time increase. Peel strength as high as 7.2−7.3 N/cm is obtained as the neutralization and catalyst time increase up to 20 min and 10 min, respectively, which is comparable to the strength achieved by the conventional laminating and sputtering processes. These improvements are probably due to an increase in the surface roughness of polyimide (PI), the activated surface condition, and the adsorption of palladium ions/atoms (Pd) on the PI surface which act as nucleation sites for Cu.

 

Key words: adhesion strength; electroless-Cu plating; flexible clad laminate; X-ray photoelectron spectroscopy

ISSN 1672-7029
CN 43-1423/U

主管:中华人民共和国教育部 主办:中南大学 中国铁道学会 承办:中南大学
湘ICP备09001153号 版权所有:《铁道科学与工程学报》编辑部
------------------------------------------------------------------------------------------
地 址:湖南省长沙市韶山南路22号 邮编:410075
电 话:0731-82655133,82656174   传真:0731-82655133   电子邮箱:jrse@mail.csu.edu.cn