Formation of unidirectional nanoporous structures in thickly anodized aluminum oxide layer
Hyun-Chae NA1, Taek-Jin SUNG1, Seok-Heon YOON1, Seung-Kyoun HYUN1, Mok-Soon KIM1,
Young-Gi LEE2, Sang-Hyun SHIN2, Se

1. Division of Materials Science and Engineering, Inha University, 253 Yonghyun-dong, Nam-gu,
Incheon, 402-751, Korea;
2. Samsung Electro-Mechanics Co., Ltd., 314, Maetan3-dong, Yeongtong-gu,
Suwon, Gyunggi-do, 443-743, Korea

Abstract:A series of anodic aluminum oxide(AAO) was grown on the commercially pure 1050 aluminum sheet by controlling electrolyte temperature (2−15 ℃) and anodizing time (0.5−6 h), using a fixed applied current density of 3 A/dm2 in diluted sulfuric acid electrolyte. A crack-free thick AAO with the thickness of 105−120 μm and containing unidirectional nano sized pores (average pore diameter of 5−7 nm) is successfully achieved in the specimens anodized for 2 h, irrespective of electrolyte temperature. When anodizing time reaches 6 h, very thick AAO with the thickness of 230−284 μm is grown, and average diameter of unidirectional pores is in the range of 6−24 nm. The higher values in both the AAO thickness and pore diameter are attained for the specimens anodized at higher temperatures of 10−15 ℃. A crack is observed to exist in the AAO after anodizing up to 4 h and more. A higher fraction (more than 9%) of the crack is shown in the specimens anodized at higher temperatures of 10−15 ℃ for 6 h and a considerable amount of giant cracks are contained.

 

Key words: aluminum; anodizing; unidirectional nanopore; anodic aluminum oxide

ISSN 1672-7029
CN 43-1423/U

主管:中华人民共和国教育部 主办:中南大学 中国铁道学会 承办:中南大学
湘ICP备09001153号 版权所有:《铁道科学与工程学报》编辑部
------------------------------------------------------------------------------------------
地 址:湖南省长沙市韶山南路22号 邮编:410075
电 话:0731-82655133,82656174   传真:0731-82655133   电子邮箱:jrse@mail.csu.edu.cn