Stress corrosion cracking of brass in ammonia solution
GUO Xian-zhong(郭献忠), GAO Ke-wei(高克玮),
QIAO Li-jie(乔利杰), CHU Wu-yang(褚武扬)

Department of Materials Physics, University of Science and Technology Beijing,
 Beijing 100083, P.R.China

Abstract:Brass foil with a protective layer formed on one side was deflected during corrosion in an ammonia solution under various applied potentials, and then corrosion-induced stress generated at brass/dezincification layer under different potentials could be measured. At the same time, susceptibility to stress corrosion cracking(SCC) of brass in the ammonia solution under various applied potentials was measured using a single-edge notched specimen. At open-circuit potential, both corrosion-induced tensile stress and susceptibility to SCC(Iσ) had a maximum value. Both tensile stress σp and susceptibility Iσ decreased slightly under anodic polarization, but reduced steeply with the decrease in potential of cathodic polarization. At the cathodic potential of -500 mV(vs SCE), corrosion-induced stress became compressive because of copper-plating layer, correspondingly, susceptibility to SCC was zero. Therefore, the variation of SCC susceptibility with potential is consistent with that of the corrosion-induced additive stress.

 

Key words: brass; corrosioninduced stress; stress corrosion cracking

ISSN 1672-7029
CN 43-1423/U

主管:中华人民共和国教育部 主办:中南大学 中国铁道学会 承办:中南大学
湘ICP备09001153号 版权所有:《铁道科学与工程学报》编辑部
------------------------------------------------------------------------------------------
地 址:湖南省长沙市韶山南路22号 邮编:410075
电 话:0731-82655133,82656174   传真:0731-82655133   电子邮箱:jrse@mail.csu.edu.cn