Stability condition of semisolid continuous casting process
XING Shu-ming(邢书明)1,ZENG Da-ben(曾大本)1,HU Han-qi(胡汉起)2
MA Jing(马  静)3,  LI Ya-min(李亚敏)3

1. Department of Mechanical Engineering, Tsinghua University,
Beijing 100084, P.R.China;
2. Foundry Institute, University of Science and Technology Beijing,
Beijing 100083, P.R.China;
3. Department of Material Science and Engineering, Hebei University of Science and Technology,
Shijiazhuang 050054, P.R.China

Abstract:The major unsteady phenomena in semisolid continuous casting process are the breakage and breakout. The essential reasons for them are the passageway blocking or the solidified shell too thin to endure the withdrawal force because of the remained shell formed at the beginning and its developing afterwards. Through theoretically analyzing the crack filling and the remained shell developing, stability conditions were presented. The essential one of them is that the stress acted on the semisolid slurry must be larger than the yield stress of it. The condition without breakage is to build a balance between the increase of the remained shell resulted in solidifying and the decrease of it resulted in flowing of the semisolid slurry. The condition without breakout is to ensure the solidified thickness larger than the safe thickness. The corresponding mathematical formulas of these conditions were set up and the verification experiments show that these conditions are reliable in applications.

 

Key words: semisolid metal; continuous casting; stability condition; breakage; breakout

ISSN 1672-7029
CN 43-1423/U

主管:中华人民共和国教育部 主办:中南大学 中国铁道学会 承办:中南大学
湘ICP备09001153号 版权所有:《铁道科学与工程学报》编辑部
------------------------------------------------------------------------------------------
地 址:湖南省长沙市韶山南路22号 邮编:410075
电 话:0731-82655133,82656174   传真:0731-82655133   电子邮箱:jrse@mail.csu.edu.cn