Twinning induced plasticity in
commercially pure titanium at lowtemperature
SUN Qiao-yan(孙巧艳), SONG Xi-ping(宋西平), GU Hai-cheng(顾海澄)

State Key Laboratory for Mechanical Behavior of Materials,
 Xi′an Jiaotong University, Xi′an 710049, P.R.China

Abstract: Using Instron 1342 at a displacement rate of 0.5 mm/min, tensile tests were conducted in hotrolled and annealed commercial pure titanium at room temperature and 77 K, respectively. Fracture surfaces and microstructures after tests were investigated by SEM and TEM respectively. The results show that both the strength and the ductility of titanium at 77 K are higher than those at room temperature. The main deformation mode of pure titanium changes from slipping at room temperature to twinning at 77 K. Twinning induced plasticity is put forward to interpret the abnormal high ductility of titanium at low temperature of 77 K.

 

Key words: titanium; mechanical properties; twinning

ISSN 1672-7029
CN 43-1423/U

主管:中华人民共和国教育部 主办:中南大学 中国铁道学会 承办:中南大学
湘ICP备09001153号 版权所有:《铁道科学与工程学报》编辑部
------------------------------------------------------------------------------------------
地 址:湖南省长沙市韶山南路22号 邮编:410075
电 话:0731-82655133,82656174   传真:0731-82655133   电子邮箱:jrse@mail.csu.edu.cn