Solidliquid state pressure bonding of Si3N4 ceramics with
aluminum based alloys and its mechanism
ZOU Gui-sheng(邹贵生), WU Ai-ping(吴爱萍), REN Jia-lie(任家烈)

Department of Mechanical Engineering,
Tsinghua University, Beijing 100084, P.R.China

Abstract:Solid-liquid state pressure bonding of Si3N4 ceramics with aluminum based alloys, which contain a small amount of intermetallic compounds Al3Ti or Al3Zr, was investigated. With this new method, the heat resistant properties of the bonding zone metal are improved, and the joints' strengths at high temperature is increased. The joints' shear strength at room temperature and at 600 ℃ reach 126~133 MPa and 32~34 MPa, respectively, with suitable bonding pressure. The reaction between aluminum and Si3N4 ceramics, which produces Al-Si-N-O type compounds is the dominant interfacial reaction, while the reactions between the second active element Ti or Zr in the aluminum based alloys and Si3N4 ceramics also occur to some extend.

 

Key words: solid-liquid state pressure bonding; Si3N4 ceramics; intermetallic compounds; high temperature properties

ISSN 1672-7029
CN 43-1423/U

主管:中华人民共和国教育部 主办:中南大学 中国铁道学会 承办:中南大学
湘ICP备09001153号 版权所有:《铁道科学与工程学报》编辑部
------------------------------------------------------------------------------------------
地 址:湖南省长沙市韶山南路22号 邮编:410075
电 话:0731-82655133,82656174   传真:0731-82655133   电子邮箱:jrse@mail.csu.edu.cn