Dry sliding wear of  MA/PM Al-10Ti alloy
WU Jin-ming(吴进明), ZHENG Shi-lie(郑史烈),
ZENG Yue-wu(曾跃武), LI Zhi-zhang(李志章)

Department of Materials Science & Engineering,
Zhejiang University, Hangzhou 310027, P.R.China

Abstract:Dry sliding wear behaviors of the Al-10Ti alloy prepared by mechanical alloying (MA) were investigated and compared with those of the alloy obtained by the rapid solidification (RS) process. The results show that, under low sliding velocity of 0.66 m/s and low applied load, the predominant wear mechanism of Al-10Ti alloy against carbon steel is adhesion. The fine dispersing reinforcement in the alloy promotes the nucleation and propagation of cracks on the subsurface, leading to a higher wear rate of MA Al-10Ti alloy, compared with that of RS Al-10Ti alloy. With increasing normal load, the formation and spallation of transfer layers on the worn surface become the predominant wear mechanism. Therefore, the wear resistance of the alloy obtained by MA surpasses that achieved by RS due to the higher strength at both ambient and elevated temperature. The wear transfer layer of the MA Al-10Ti alloy is determined to be consisted mainly of Fe2O3 and metal Fe.

 

Key words: Al-Ti alloy; sliding wear; mechanical alloying; rapid solidification(RS)

ISSN 1672-7029
CN 43-1423/U

主管:中华人民共和国教育部 主办:中南大学 中国铁道学会 承办:中南大学
湘ICP备09001153号 版权所有:《铁道科学与工程学报》编辑部
------------------------------------------------------------------------------------------
地 址:湖南省长沙市韶山南路22号 邮编:410075
电 话:0731-82655133,82656174   传真:0731-82655133   电子邮箱:jrse@mail.csu.edu.cn