Particle melting, flattening, and
stacking behaviors in induction
plasma deposition of tungsten
JIANG Xian-liang(蒋显亮)1, M. I. Boulos1,2

1. Institute of Surface and Coatings Technology,
Central South University, Changsha 410083, P.R.China;
2. Department of Chemical Engineering, University of Sherbrooke,
Sherbrooke, J1K 2R1, Canada

Abstract: Particle melting, flattening, and stacking behaviors during induction plasma deposition of refractory tungsten were studied for land-based turbine engine application. Scanning electron microscopy was used to observe the morphology of particles and splats as well as to examine the microstructure of tungsten deposit. Three kinds of pores were found in the deposit, i.e., large pores with d >10μm, medium pores in the range of 1~10μm, and small pores withd <1μm. Both optimized plasma spray condition and use of spherical powder with a narrow particle size distribution are important in the elimination of large and medium pores and have significant influences on the formation of dense tungsten deposit. Highly dense tungsten deposit was obtained through complete melting, sufficiently flattening, and regularly stacking of tungsten particles.

 

Key words: induction plasma; tungsten; deposition

ISSN 1672-7029
CN 43-1423/U

主管:中华人民共和国教育部 主办:中南大学 中国铁道学会 承办:中南大学
湘ICP备09001153号 版权所有:《铁道科学与工程学报》编辑部
------------------------------------------------------------------------------------------
地 址:湖南省长沙市韶山南路22号 邮编:410075
电 话:0731-82655133,82656174   传真:0731-82655133   电子邮箱:jrse@mail.csu.edu.cn