Fabrication and fracture analysis of
MoSi2 matrix composites by mechanical alloying
MA Ying(马  颖)1, HAO Yuan(郝  远)1, ZHANG De-liang(张德良)2, YU Ning(余  宁)1

1. School of Materials Science & Engineering, Gansu University of Technology,
Lanzhou 730050, P.R.China;
2. Department of Materials and Process Engineering, University of Waikoto,
Hamilton 3150, New Zealand

Abstract: Four composites, MoSi2+ZrO2, MoSi2+ZrO2(Y2O3), MoSi2+ZrO2+SiC and MoSi2+ZrO2(Y2O3)+SiC are fabricated by mechanical alloying. It is clear that cracks produced on the MoSi2 matrix composites during hardness testing belong to the Palmquist crack system. The value of highest fracture toughness of MoSi2+ZrO2+SiC composite is 7.58?MPa·m1/2, which is nearly three times that of monolithic MoSi2. This can be attributed to well-distributed ZrO2 and SiC particles along the boundaries of very fine MoSi2 grains.

 

Key words:  mechanical alloying; composites; fracture toughness; MoSi2; ZrO2; Y2O3

ISSN 1672-7029
CN 43-1423/U

主管:中华人民共和国教育部 主办:中南大学 中国铁道学会 承办:中南大学
湘ICP备09001153号 版权所有:《铁道科学与工程学报》编辑部
------------------------------------------------------------------------------------------
地 址:湖南省长沙市韶山南路22号 邮编:410075
电 话:0731-82655133,82656174   传真:0731-82655133   电子邮箱:jrse@mail.csu.edu.cn