Solid-state synthesis of Sr- and Co-doped LaMnO3 perovskites
MA Wen-hui(马文会), XIE Gang(谢  刚), CHEN Shu-rong(陈书荣), CUI Heng(崔  衡)

Faculty of Materials and Metallurgical Engineering,
Kunming University of Science and Technology, Kunming 650093, P.R.China

Abstract:  The synthesis process for La1-xSrxMn1-yCoyO3-δ(x =0.2, 0.3;y =0.2, 0.8,designated as LSMC below) perovskite oxides prepared by solid state reaction was investigated using DSC/TG, XRD, EPMA and particle size analysis methods. It was found that LSMCs were all of single phase and the synthesis process might be divided into three stages: the decomposition of reactants, the formation of LaMn(Co)O3-based oxides, and the formation of LSMC solid solution. Typical average and the peak value of particle size, and the specific surface area are 14.65μm,16.4μmand 1.38m2/mL,respectively, for mixed reactants and are 23.81μm, 32.11μmand 0.5m2/mL, respectively, for powder synthesized at 1200℃for 8hin air.

 

Key words:   solidstate reaction synthesis; La1-xSrxMn1-yCoyO3; perovskite; intermediate temperature SOFCs

ISSN 1672-7029
CN 43-1423/U

主管:中华人民共和国教育部 主办:中南大学 中国铁道学会 承办:中南大学
湘ICP备09001153号 版权所有:《铁道科学与工程学报》编辑部
------------------------------------------------------------------------------------------
地 址:湖南省长沙市韶山南路22号 邮编:410075
电 话:0731-82655133,82656174   传真:0731-82655133   电子邮箱:jrse@mail.csu.edu.cn