Coordination and bond properties of Al and
Si ions in system of Al2O3-SiO2 melts
WU Yong-quan(吴永全), HOU Huai-yu(侯怀宇), CHEN Hui(陈  辉),
YOU Jing-lin(尤静林), JIANG Guo-chang(蒋国昌)

Shanghai Enhanced Laboratory of FerroMetallurgy,
Shanghai University, Shanghai 200072, P.R.China

Abstract: The coordination and bond properties of aluminium and silicon ions were discussed by means of molecular dynamics simulation. By combining KA and MATSUMIYA potentials, the results of simulations agree better with the experiments. Trend of coordination and bond properties changing along with the increasing content Al2O3 from 0 to 100%(mole fraction) was obtained. Average bond lengths of Si-O in these simulations are within the range of 1.60~1.63Å and become smaller from 1.63Å in sample 0 to 1.60Å in sample 9 along with increasing content of Al2O3. Average bond lengths of Al-O are within the range from 1.77Å in sample 1 to 1.86Å in sample 10. By analyzing therelation of CN(T) and CNSi(T) with Si/(Si+Al), it is found that Al mainly locates on the tetrahedral sites which neighbor the Si tetrahedra but avoid the Al tetrahedra while alumina content is low. Whereas when Si/(Si+Al)<0.5, Al-octahedral units appeared and became predominant gradually. Meanwhile, Al avoidance principle can only be maintained at low alumina content. With increasing alumina, this principle would be broken gradually.

 

Key words:  Al2O3-SiO2 melts; coordination and bond properties;  molecular dynamics simulation

ISSN 1672-7029
CN 43-1423/U

主管:中华人民共和国教育部 主办:中南大学 中国铁道学会 承办:中南大学
湘ICP备09001153号 版权所有:《铁道科学与工程学报》编辑部
------------------------------------------------------------------------------------------
地 址:湖南省长沙市韶山南路22号 邮编:410075
电 话:0731-82655133,82656174   传真:0731-82655133   电子邮箱:jrse@mail.csu.edu.cn