Metastable phase transitions in 
Mo-Si and V-Si systems activated 
by high energy ball milling
LIU Lin(柳  林)

The State Key Lab of Plastic Forming Stimulation and Die & Mould Technology,
Huazhong University of Science and Technology,Wuhan 430074,China

Abstract:Mechanical alloying of Mo-Si (Mo33Si67) and V-Si (V75Si25) powder mixtures was activated by high energy ball milling at ambient temperature.The metastable phase transitions in both systems during milling were investigated by X-ray diffraction, scanning and transmission electron microscopy.It is found that the alloying processes are closely related to the milling conditions.As far as the Mo-Si system is concerned,ball milling leads to the formation of both α-MoSi2 (room temperature phase) and β-MoSi2 (high temperature phase),but lower energy milling favors the formation of β phase,while higher energy milling promotes the formation of α phase.In addition,if the milling energy is high enough,the Mo/Si reaction is governed by ase lf-propagating high temperature process.On the other hand, two different pathways of phase transition in the V-Si system were also identified depending on the milling intensity,i.e.weak milling leads to amorphous transition, whereas intensive milling causes the formation of V3Si and V5Si3 intermetallic compounds.Finally,the thermodynamics and kinetics related to the different phase transitions in the two systems were discussed.

 

Key words: mechanical alloying;phase transitions;energy transfer;Mo-Si;V-Si

ISSN 1672-7029
CN 43-1423/U

主管:中华人民共和国教育部 主办:中南大学 中国铁道学会 承办:中南大学
湘ICP备09001153号 版权所有:《铁道科学与工程学报》编辑部
------------------------------------------------------------------------------------------
地 址:湖南省长沙市韶山南路22号 邮编:410075
电 话:0731-82655133,82656174   传真:0731-82655133   电子邮箱:jrse@mail.csu.edu.cn