Synthesis and properties of rubber-steel cord
adhesion promoter nickel borate a cylate
LI Xiao-ru(李晓如),WU Hai-ying(吴海鹰),CHENG Ben-cheng(成本诚)

College of Chemistry and Chemical Engineering, 
Central South University, Changsha 410083, China

Abstract:The synthesis of nickel borate acylate (NBA),a kind of rubber-steel cord adhesion promoter (AP),through nickel carbonate, borate and mixed carboxylic acid was studied. Nickel carbonate could be prepared by the reaction of nickel sulfate with sodium carbonate in aqueous solution. After strong stirring for 2h, the mixed nickel carboxylate could be synthesized by the reaction of nickel carbonate with isooctanoic acid and acetic acid. The mole ratio of these chemicals was 1∶1∶1.1. NBA was synthesized by reaction of mixed nickel carboxylate with tributyl borate under strong stirring at 200~250℃ for 6h. By detecting and comparing with 680C product from Manobond Company of England, the NBA synthesized through isooctanoic acid and tributyl borate is very similar with 680C in IR data, 300% fixed extension strength, tensile strength,hardness and cure curve. However, tensile failure extensibility and hot air aging of NBA are a little lower than those of 680C. The experimental results show that NBA can be used as rubber-steel cord AP.

 

Key words: nickel borate acylate;adhesion promoter;nickel carbonate;borate

ISSN 1672-7029
CN 43-1423/U

主管:中华人民共和国教育部 主办:中南大学 中国铁道学会 承办:中南大学
湘ICP备09001153号 版权所有:《铁道科学与工程学报》编辑部
------------------------------------------------------------------------------------------
地 址:湖南省长沙市韶山南路22号 邮编:410075
电 话:0731-82655133,82656174   传真:0731-82655133   电子邮箱:jrse@mail.csu.edu.cn