High temperature oxidation behaviors of
Ti-Cr alloys with Laves phase TiCr2
XIAO Ping-an(肖平安)12, QU Xuan-hui(曲选辉)1,3
LEI Chang-ming(雷长明)1, ZHU Bao-jun(祝宝军)1
QIN Ming-li(秦明礼)1

1.State Key Laboratory for Powder Metallurgy,
Central South University, Changsha 410083, China;
2.Department of Automobile and Electromechanical Engineering,
Changsha Communications University, Changsha 410076, China;
3. School of Materials Science and Engineering, University of
Science and Technology Beijing, Beijing 100083, China

Abstract:The high temperature oxidation behaviors of Ti-Cr alloys containing 18%~35%Cr with Laves phase TiCr were investigated at 650~780℃ for exposure up to 104h. The results reveal that chromium content has critical significance to the oxidation resistance of the alloys. The scaling rates of the alloys with less than 21%Cr are higher than those measured for pure titanium, but for the alloys with more than 26%Cr their scaling rate is lowered by 1~2 times, under the same oxidizing conditions. Both an external and an internal oxidation layers were observed. The oxidation resistance enhancement by chromium alloying is contributed to the formation of a continuous and compact chromic oxide interleaf in the scale. Oxidation temperature significantly affects the scaling rates of Ti-Cr alloys, and the mass gain is doubled with a temperature change from 650℃ to 700℃ or from 700℃ to 780℃, for the same exposure duration. TiCr2 shows no negative influence on the high temperature oxidation resistance of the alloys.

 

Key words: Laves phase; TiCr2;Ti-Cr alloy;oxidation

ISSN 1672-7029
CN 43-1423/U

主管:中华人民共和国教育部 主办:中南大学 中国铁道学会 承办:中南大学
湘ICP备09001153号 版权所有:《铁道科学与工程学报》编辑部
------------------------------------------------------------------------------------------
地 址:湖南省长沙市韶山南路22号 邮编:410075
电 话:0731-82655133,82656174   传真:0731-82655133   电子邮箱:jrse@mail.csu.edu.cn