Recycling high density tungsten alloy
powder by oxidization-red uction process
ZHANG Zhao-sen(张兆森),CHEN Li-bao(陈立宝),
HE Yue-hui(贺跃辉),HUANG Bai-yun(黄伯云)

State Key Laboratory for Powder Metallurgy,
Central South University, Changsha 410083, China

Abstract:The processes of directly recycling high density tungsten alloy by oxidation-reduction technique were investigated. The particle size of recycled powder is fine, and the shape of powder particle is regular when the final reduction temperature is 850℃, in which the average size of the tungsten alloy p articles reduced is about 1.5μm. The average size of the alloy particles increase to 6μm and 9μm when increasing the reduction temperature to 900℃ and 950℃, respectively. However, if the reduction temperature is higher than 900℃, the surface feature of powder is complicated. Increasing reduction temperature from 900℃ to 950℃, the content o f oxygen of recycled powder decreases from 0.2314% to 0.1700%, and powder particles grow slightly. It has been also found that the chemical composition of the recycled alloy powder is the same as the initial powder.

 

Key words: tungsten alloy; oxidation-reduction process; recycle; saving environment

ISSN 1672-7029
CN 43-1423/U

主管:中华人民共和国教育部 主办:中南大学 中国铁道学会 承办:中南大学
湘ICP备09001153号 版权所有:《铁道科学与工程学报》编辑部
------------------------------------------------------------------------------------------
地 址:湖南省长沙市韶山南路22号 邮编:410075
电 话:0731-82655133,82656174   传真:0731-82655133   电子邮箱:jrse@mail.csu.edu.cn