Friction and wear properties of
pitch/resin densified carbon-carbon
 composites used for airbrakes
GONG Qian-ming(巩前明), HUANG Bai-yun(黄伯云),
HUANG Qi-zhong(黄启忠), LI Jiang-hong(李江鸿),
WU Feng-qiu(吴凤秋), LI Ye(李  晔)

State Key Laboratory for Powder Metallurgy,
Central South University, Changsha 410083, China

Abstract:By use of X-ray diffractometry and scanning electron microscope (SEM), the friction and wear results obtained from MM-1000 dynamometer tests of CVI pitch/ resin C/C composites were analyzed. By investigating the factors that affected t he friction and wear properties, such as matrix carbon, application environment, graphitization degree and brake pressure, etc, friction and wear mechanism of carbon materials were probed. The results indicate that pitch densified CVI initially treated composite is more graphitizable with its graphitization degree up to 62%, and which results in uniform small debris easier to generate, more smooth friction curves with the coefficient of 0.3~0.4 and relatively higher linear wear and mass loss, compared with CVI/resin C/C composites. It was further proved by SEM observation that tribological behavior of C/C composite w as system dependent. Factors determining the friction and wear properties such as the size of debris and its influence on friction and wear, brake pressure, graphization degree and debris film formation interacted and affected each other. The friction and wear mechanism of C/C composites under different high temperature treatments needs further research.

 

Key words: C/C composites; friction; wear debris; pitch; resin

ISSN 1672-7029
CN 43-1423/U

主管:中华人民共和国教育部 主办:中南大学 中国铁道学会 承办:中南大学
湘ICP备09001153号 版权所有:《铁道科学与工程学报》编辑部
------------------------------------------------------------------------------------------
地 址:湖南省长沙市韶山南路22号 邮编:410075
电 话:0731-82655133,82656174   传真:0731-82655133   电子邮箱:jrse@mail.csu.edu.cn