Anisotropic plastic deformation behavior of
B2-ordered Fe3Al single crystals at
room temperature
ZHENG Wei-wei(郑为为)1,YANG Wang-yue(杨王王月)2
SUN Zu-qing(孙祖庆)1

1. State Key Laboratory for advanced Metals and Materials,
University of Science & Technology Beijing,Beijing 100083, China;
2. School of Materials Science and Engineering,University of Science &
Technology Beijing,Beijing 100083, China

Abstract:The tensile plastic deformation behavior of B2-ordered Fe3Al single crystals at room temperature was systematically investigated. The results show that the mechanical properties are strongly orientation dependent. The plastic elongation of crystals with orientation near [110] is as high as 42%. Slip trace analysis shows that although slip planes are found to change among {110}, {112} and {123} with the change in orientations, the initial slip planes in allcases are {110}. Five-stage work hardening curve including four linear stages and one parabolic stage is obtained; but not all stages are observed in the actual deformation of each crystal. In combination with investigations of dislocation substructure, it is found that deformations in stage Ⅰ~Ⅲ are corresponding to the motion of two-fold superdislocations. The higher work hardening rate of stage Ⅱis mainly due to the stronger interactions between primary dislocations and secondary dislocations than those in stage Ⅲ. Deformation in stage  involved is not only the motion of two-fold superdislocations but also the slip of dissociated superpartials with APB traps and the formation of APB tube, both of which are attributed to the hardening. Deformation in stage  Ⅴ is controlled by the cross slip of dissociated superpartials. The dominated softening effect of cross slip reduces the hardening rate and leads to the formation of parabolic stage.

 

Key words: plastic deformation; B2-order; Fe3Al; single crystal

ISSN 1672-7029
CN 43-1423/U

主管:中华人民共和国教育部 主办:中南大学 中国铁道学会 承办:中南大学
湘ICP备09001153号 版权所有:《铁道科学与工程学报》编辑部
------------------------------------------------------------------------------------------
地 址:湖南省长沙市韶山南路22号 邮编:410075
电 话:0731-82655133,82656174   传真:0731-82655133   电子邮箱:jrse@mail.csu.edu.cn