High temperature creep behavior of
in-situ synthesized MoSi2-30%SiC composite
FU Xiao-wei(傅晓伟)1, YANG Wang-yue(杨王王月)1, SUN Zu-qing(孙祖庆)2,
ZHANG Lai-qi(张来启)2, ZHU Jing(朱  静)3

1. School of Materials Science & Engineering, University of Science &
Technology Beijing, Beijing 100083, China;
2. State Key Laboratory for Advanced Metals and Materials,
University of Scie nce & Technology Beijing, Beijing 100083, China;
3. Department of Materials Science & Engineering, Tsinghua University, 
Beijing 1 00084, China

Abstract:The compressive creep behavior at 1200~1400℃ of an in-situ synthesized MoSi2-30%SiC (volume fraction) composite and a traditional PM MoSi2-30%SiC (volume fraction) composite is investigated. The creep rate of the in-situ synthesized MoSi2-30%SiC (volume fraction) composite is about 10-7s-1 under stress of 60~120MPa, and significantly lower than that made by PM method above 1300℃. The reason is that the interface between SiC particle and MoSi2 matrix in in-situ synthesized SiCp/MoSi2 is of direct atomic bonding without any amorphous glassy phase, such as SiO2 structure. Creep deformation occurs primarily by dislocation motion and the dislocations have Burgers vectors of the type of 〈110〉 and 〈100〉.

 

Key words: SiC/MoSi2 composite; in-situ synthesis; creep; dislocation

ISSN 1672-7029
CN 43-1423/U

主管:中华人民共和国教育部 主办:中南大学 中国铁道学会 承办:中南大学
湘ICP备09001153号 版权所有:《铁道科学与工程学报》编辑部
------------------------------------------------------------------------------------------
地 址:湖南省长沙市韶山南路22号 邮编:410075
电 话:0731-82655133,82656174   传真:0731-82655133   电子邮箱:jrse@mail.csu.edu.cn