Fabrication of sintered Zn-27%Al and
comparison of its tribological
behavior with cast alloy
Ngai Tungwai Leo(倪东惠), LONG Yan(龙  雁), ZHANG Da-tong(张大童), 
LUO Zong-qiang(罗宗强), ZHANG Wen(张  文)

College of Mechanical Engineering, South China University of Technology,
Guangzhou 510640, China

Abstract:High quality Zn-base powder with low oxygen content, fine particle size and fine microstructure can be obtained by gas atomization using nitrogen. Cast and sintered Zn-27%Al alloys (ZMJ) were prepared. Tribological behaviors of the cast and sintered alloys under lubricated and nonlubricated conditions were studied and compared. Worn surfaces and microstructures of these alloys were examined. Results indicate that although the strength of the sintered alloy is considerably less than that of the cast alloy, the sintered alloy has a better wear resistance. The fine microstructure obtained by rap id solidification is beneficial to the wear-resisting property. The wear volume of sintered ZMJ is only 36% and 59% of the wear volume that found in cast ZMJ under non-lubricated and lubricated conditions, respectively. For lubricated wear test, abrasive wear is the major wear mechanism and for non-lubricated wear test, oxidation wear and adhesive wear are the major wear mechanisms.

 

Key words: powder metallurgy; Zn-27%Al; tribological behavior; intermetallic phases; undulated surface

ISSN 1672-7029
CN 43-1423/U

主管:中华人民共和国教育部 主办:中南大学 中国铁道学会 承办:中南大学
湘ICP备09001153号 版权所有:《铁道科学与工程学报》编辑部
------------------------------------------------------------------------------------------
地 址:湖南省长沙市韶山南路22号 邮编:410075
电 话:0731-82655133,82656174   传真:0731-82655133   电子邮箱:jrse@mail.csu.edu.cn