Mechanism of strengthening of cube texture for high purity aluminum foils by additional-annealing
ZHANG Xin-ming(张新明), LIU Sheng-dan(刘胜胆),
TANG Jian-guo(唐建国), ZHOU Zhuo-ping(周卓平)

School of Materials Science and Engineering,
Central South University, Changsha 410083, China

Abstract:The mechanism of strengthening of cube texture ({001}〈100〉) by additional-annealing of high purity aluminum foils was investigated by using orientation distribution functions (ODFs) and electron back scattered diffraction (EBSD). The results of ODFs and fiber show that the orientation densities of the S {123}〈634〉 and Cu {112}〈111〉 components increase in both the additional-annealed samples and the 0.11mm final cold-rolled foils. And the EBSD results demonstrate that cube nuclei can be identified in the deformed matrix of those additional-annealed samples. It is suggested that the strengthening of cube texture can be brought out by the increasing of components of S and Cu and the formation of cube nuclei caused by additional-annealing. Moreover, it is found that the cube texture increases first and then decreases with increasing additional-annealing temperature, and it is the strongest at 180℃.The strengthening of cube texture by additional-annealing is proposed as the result of oriented growth of cube subgrains.

 

Key words:  high purity aluminum foils; additional-annealing; cube texture; ODF; EBSD

ISSN 1672-7029
CN 43-1423/U

主管:中华人民共和国教育部 主办:中南大学 中国铁道学会 承办:中南大学
湘ICP备09001153号 版权所有:《铁道科学与工程学报》编辑部
------------------------------------------------------------------------------------------
地 址:湖南省长沙市韶山南路22号 邮编:410075
电 话:0731-82655133,82656174   传真:0731-82655133   电子邮箱:jrse@mail.csu.edu.cn