Mechanical properties of hot rolled
 2519 aluminum alloy plate
PENG Da-shu(彭大暑), CHEN Xian-feng(陈险峰),
LIN Qi-quan(林启权), ZHANG Hui(张 辉)

School of Materials Science and Engineering,
Central South University, Changsha 410083, China

Abstract:The effects of differences of temper on mechanical properties of T6, T7 and T8 plates of aluminum alloy 2519 were studied. The stress corrosion cracking(SCC) sensitivity was evaluated with parameters such as Kσ and Kδ.Tensile tests were divided into two groups: one was performed on tensile specimens without pre-corrosion, the other was performed on tensile specimens which were pre-corroded in 3.5%NaCl+1%H2O2 solution at 25℃.The results show that SCC resistance of alloy 2519 ranks in the order of T8>T7>T6 and the mechanical properties rank in the order of T6>T8>T7. SEM fractographs of the failed specimen show that the SCC sensitivity can be determined by the distribution of the second phase particles and size and the shape of grains in the alloy.

 

Key words:  2519 aluminum alloy; stress corrosion cracking sensitivity; strength; elongation; temper

ISSN 1672-7029
CN 43-1423/U

主管:中华人民共和国教育部 主办:中南大学 中国铁道学会 承办:中南大学
湘ICP备09001153号 版权所有:《铁道科学与工程学报》编辑部
------------------------------------------------------------------------------------------
地 址:湖南省长沙市韶山南路22号 邮编:410075
电 话:0731-82655133,82656174   传真:0731-82655133   电子邮箱:jrse@mail.csu.edu.cn