Ambient temperature cured TiB2 cathode coating  for aluminum electrolysis
LAI Yan-qing(赖延清)1, LI Qing-yu(李庆余)1,2,
YANG Jian-hong(杨建红)1, LI Jie(李 劼)1

1. School of Metallurgical Science and Engineering,
Central South University, Changsha 410083, China;
2. Chemistry Department, Guangxi Normal University, Guilin 5410043, China

Abstract:The concept of ambient temperature curable TiB2 cathode coating was put forward, and the ambient temperature curable TiB2 cathode coating was prepared successfully. Differing from the previous TiB2 cathode coating solidified approximately at 200℃,the ambient temperature curable TiB2 cathode coating can be solidified at room temperature, so the heating equipment is not necessary, which simplifies the preparation process and facilitates the industrial application of TiB2 cathode coating. Many kinds of resin and curing agent were investigated. On the above-mentioned basis, the ambient temperature curable TiB2 cathode coating was prepared with furan resin 5500 mixed with complex resins B as carbon binder and DXG1 as curing agent in 24h. The results show that the properties of prepared coating are excellent, the electrical resistivity is 29.8μΩ·m, the compressive strength is 33.6MPa, which are all better than the relevant properties of partially graphitized cathode carbon block for aluminum electrolysis prescribed by the GB 8744-88. SEM morphologies show that the section morphology of the TiB2 coating is unaltered during the electrolysis test, the TiB2 coating can be used in aluminum electrolysis industry to save energy and prolong the life of aluminum electrolysis cell.

 

Key words:  ambient temperature solidification; TiB2 cathode coating; aluminum electrolysis

ISSN 1672-7029
CN 43-1423/U

主管:中华人民共和国教育部 主办:中南大学 中国铁道学会 承办:中南大学
湘ICP备09001153号 版权所有:《铁道科学与工程学报》编辑部
------------------------------------------------------------------------------------------
地 址:湖南省长沙市韶山南路22号 邮编:410075
电 话:0731-82655133,82656174   传真:0731-82655133   电子邮箱:jrse@mail.csu.edu.cn