Effect of Zr on behavior of compressive creep in as cast ZA27 alloy
WEI Xiao-wei(魏晓伟)1,2, SHEN Bao-luo(沈保罗)1

1. Department of Metal Materials, Sichuan University,
Chengdu 610065, China;
2. Department of Materials Science and Engineering,
Sichuan Institute of Technology, Chengdu 610039,China

Abstract:The effect of Zr on the behavior of compressive creep in as cast ZA27 alloy was investigated in the temperature range of 20-160℃ and under different compressive stresses in the range of 50-137.5MPa with special apparatus. The results show that the primary compressive creep strains and steady creep rates of ZA27-Zr alloy and ZA27 alloy increase with increasing temperature and stress. However, the primary compressive creep strain and steady creep rate of the ZA27-Zr alloy are lower than that of the ZA27 alloy below 100℃, but higher at 160℃. The compressive creep behaviors in both ZA27-Zr alloy and ZA27 alloy obey an empirical equation lnt=Cnlnσ+QRT, and the exponent stress n is 3.63 for ZA27-Zr alloy and 3.46 for ZA27 alloy, respectively, the activation energy Q is 87.32kJ/mol for ZA27-Zr alloy and 81.09kJ/mol for ZA27 alloy. Different material structural constants are associated with different compressive creep behaviors in the alloy. The compressive creep rate in the alloy is controlled by the lattice diffusion of zinc and dislocation limb.

 

Key words:  as cast ZA27 alloy; Zr; compressive creep; stress exponent; activation energy

ISSN 1672-7029
CN 43-1423/U

主管:中华人民共和国教育部 主办:中南大学 中国铁道学会 承办:中南大学
湘ICP备09001153号 版权所有:《铁道科学与工程学报》编辑部
------------------------------------------------------------------------------------------
地 址:湖南省长沙市韶山南路22号 邮编:410075
电 话:0731-82655133,82656174   传真:0731-82655133   电子邮箱:jrse@mail.csu.edu.cn