Nanostructured bulk glassy Cu60Zr30Ti10 alloy with high strength and good ductility in cast state
CHEN Yan-tang(陈颜堂)1,2, ZHANG Tao(张 涛)1,
ZHANG Wei(张 伟)1, INOUE Akihisa1,DING Qing-feng(丁庆丰)2

1. Institute for Materials Research,
Tohoku University, Sendai 980-8577, Japan;
2. National Enterprise Technology Center,
Wuhan Iron and Steel(Group)Co., Wuhan 430080, China

Abstract:The bulk glassy Cu60Zr30Ti10 alloy with a diameter up to 4mm and a length of 70mm containing nanocrystalline phase was successfully developed by using copper mold casting method. The temperature interval of the supercooled liquid region before crystallization is above 37K. The glass transition temperature (Tg) and the reduced glass transition temperature (Tg/Tl) of the cast bulk glassy Cu60Zr30Ti10 alloy are 713K and 0.62. The cast bulk glassy alloy, which has high glassy forming ability, shows expected mechanical properties. The elastic modulus, yield strength, fracture strength and elongation including elastic elongation are 114GPa, 1785MPa, 2150MPa and 3.3% respectively in compressive deformation, and 112GPa, 1780MPa,2000MPa and 1.9% respectively in tensile deformation. High resolution transmission electron microscope (HRTEM) and nano-beam electron diffraction (NBED) studies indicate that the cast metallic bulk glassy Cu60Zr30Ti10 alloy consists of nanocrystals with a size of -4nm embedded in glassy matrix. The nanoparticle is identified as CuZr and has point space group symmetry of pm3-mand its lattice parameter is a=0.3262nm . The nanocrystalline phase grew up to 10nm upon annealing at 430℃ for 10min and caused the alloy brittle.

 

Key words: bulk glassy Cu60Zr30Ti10 alloy; casting; microstructure; nanocrystalline phase; mechanical property

ISSN 1672-7029
CN 43-1423/U

主管:中华人民共和国教育部 主办:中南大学 中国铁道学会 承办:中南大学
湘ICP备09001153号 版权所有:《铁道科学与工程学报》编辑部
------------------------------------------------------------------------------------------
地 址:湖南省长沙市韶山南路22号 邮编:410075
电 话:0731-82655133,82656174   传真:0731-82655133   电子邮箱:jrse@mail.csu.edu.cn