Flow stress and microstructural evolution in as rolled AZ91 alloy during hot deformation
ZHOU Hai-tao(周海涛)1, WANG Qu-dong(王渠东)1, WEI Yin-hong(尉胤红)1, DING Wen-jiang(丁文江)1, ZHU Yan-ping(朱燕萍)1, Y. Chino2, M. Mab

1. National Engineering Research Center of Light Alloys Net Forming, 
School of Materials Science and Engineering, Shanghai Jiaotong University,
 Shanghai 200030, China;
2. Institute for Structural and Engineering Materials, Nagoya 462-8510, Japan

Abstract:The flow stress behavior and microstructural evolution in as rolled AZ91 alloy were studied by tensile test at temperature ranging from 573K to 698K and with initial strain rate of 10-3-1s-1. The results show that the activation energy of the AZ91 alloy is 96kJ/mol and the stress exponent is 3.5.Grain refinement is observed during hot deformation. It is found that grain refinement is due to dynamic recrystallization, but grain size is decreased with increasing Zener-Hollomon parameter. The deformation mechanism is dislocation cross-slip, dislocation climbs and twin intersections, which are probably suitable to the development of substructures. Twins always exist in matrix whether they are at high temperature or at low temperature. Strain induced precipitation of Mg17Al12 occurs in the AZ91 alloy and stabilizes the subgrain boundaries. 

 

Key words: magnesium alloy; grain refinement; recrystallization; strain softening;strain hardening

ISSN 1672-7029
CN 43-1423/U

主管:中华人民共和国教育部 主办:中南大学 中国铁道学会 承办:中南大学
湘ICP备09001153号 版权所有:《铁道科学与工程学报》编辑部
------------------------------------------------------------------------------------------
地 址:湖南省长沙市韶山南路22号 邮编:410075
电 话:0731-82655133,82656174   传真:0731-82655133   电子邮箱:jrse@mail.csu.edu.cn