Electrochemical characteristics and surface morphology in non-chromate chemical conversion coating for Zn-electroplated steel sheets
Masazumi OKIDO1, Ryoichi ICHINO1, Seok-Ki JANG2, Seong-Jong KIM2

1. Graduate School of Engineering, Nagoya University, Furo-cho, Chikusa-ku, Nagoya 464-8603, Japan;
2. Division of Marine Engineering, Mokpo Maritime University, Mokpo City, Jeonnam 530-729, Korea

Abstract:The corrosion protection property and morphology of colloidal silica conversion films as an alternative to chemical conversion coating(CCC) films were examined. The corrosion behavior was investigated in 3%NaCl solution using electrochemical techniques. Corrosion was implied by the appearance of red rust on the specimen surface. The results show that in 3%NaCl solution, red rust appears at 15−20, 55−70, and 75−85 d on Zn-electroplated steel, colloidal silica conversion-coated specimens, and chemical conversion-coated, specimens, respectively. In the salt spray test, the colloidal silica film provides better corrosion protection than CCC film, i.e., red rust appears at 96 h on the Zn-electroplated steel sheet, at 432 h on the CCC films, and at 888 h on silica conversion coating.

 

Key words: colloidal silica conversion film, corrosion salt spray test, rust

ISSN 1672-7029
CN 43-1423/U

主管:中华人民共和国教育部 主办:中南大学 中国铁道学会 承办:中南大学
湘ICP备09001153号 版权所有:《铁道科学与工程学报》编辑部
------------------------------------------------------------------------------------------
地 址:湖南省长沙市韶山南路22号 邮编:410075
电 话:0731-82655133,82656174   传真:0731-82655133   电子邮箱:jrse@mail.csu.edu.cn