Electrodeposited Ni, Fe, Co and Cu single and
multilayer nanowire arrays on anodic aluminum oxide template
Bobomurod HAMRAKULOV1, In-Soo KIM1, M. G. LEE1, B. H. PARK2

1. School of Advanced Materials and Systems Engineering, Kumoh National Institute of Technology,
 Gumi, Gyung Buk, 730-701, Korea;
2. Smart Applications Co. LTD, Cheonan, Chungnam, 330-814, Korea

Abstract:The Ni, Fe, Co and Cu single and multilayer nanowire arrays to make perpendicular magnetic recording media were fabricated with nanoporous anodic aluminum oxide (AAO) templates from Watt solution and additives by the DC electrodeposition. The results show that the diameters of Ni, Fe, Co and Cu single and multilayer nanowires in AAO templates are 40−80 nm and the lengths are about 30 μm with the aspect ratio of 350−750. The magnetic properties of the prepared nanowires are different under different electrodepositing conditions. The remanences (Br) of Ni/Cu/Fe multilayer nanowires are lower than those of others multilayer nanowires, and coercivity (Hc) of Ni/Cu/Fe multilayer nanowires are lower than those of others multilayer nanowires. These are compatible with the required conditions of high density magnetic media devices that should have the low coercivity to easily success magnetization and high remanence to keep magnetization after removal of magnetic field.

 

Key words: anodic aluminum oxide (AAO); nanowire; Ni; Fe; Co; Cu; magnetic property; electrodeposition

ISSN 1672-7029
CN 43-1423/U

主管:中华人民共和国教育部 主办:中南大学 中国铁道学会 承办:中南大学
湘ICP备09001153号 版权所有:《铁道科学与工程学报》编辑部
------------------------------------------------------------------------------------------
地 址:湖南省长沙市韶山南路22号 邮编:410075
电 话:0731-82655133,82656174   传真:0731-82655133   电子邮箱:jrse@mail.csu.edu.cn