TEM study on microstructures and properties of
7050 aluminum alloy during thermal exposure
SHEN Kai(沈凯)1 , CHEN Jin-ling(陈金灵)1, YIN Zhi-min(尹志民)2

1. School of Materials Science and Technology, Nanjing University of Aeronautics and Astronautics,
 Nanjing 210016, China;
2. School of Materials Science and Engineering, Central South University, Changsha 410083, China

Abstract:The microstructures of 7050 aluminum alloy under different thermal exposure conditions were investigated by means of transmission electron microscopy (TEM), high resolution electron microscopy (HREM) and tensile test. Guinier preston (GP) zone and h′ phase are the main precipitates in original 7050 alloy. The orientation relationship between h′ and matrix is  and . When the alloy is exposed at different temperatures for 500 h, with the thermal exposure temperature increasing, it can be seen under TEM that the precipitates become larger and the width of precipitate free zones (PFZ) becomes larger. The higher temperature the alloy is exposed at, the more the strength is reduced. Both GP zones and h′ precipitates getting coarser and the PFZ getting wider should be responsible for the strength decline and elongation rise of 7050 alloy during thermal exposure.

 

Key words: 7050 aluminum alloy; thermal exposure; microstructure

ISSN 1672-7029
CN 43-1423/U

主管:中华人民共和国教育部 主办:中南大学 中国铁道学会 承办:中南大学
湘ICP备09001153号 版权所有:《铁道科学与工程学报》编辑部
------------------------------------------------------------------------------------------
地 址:湖南省长沙市韶山南路22号 邮编:410075
电 话:0731-82655133,82656174   传真:0731-82655133   电子邮箱:jrse@mail.csu.edu.cn