Deformation behavior of fine-grained 5083 Al alloy at elevated temperature
ZHANG Kai-feng(张凯锋), YAN Hong-hua(闫宏华)

School of Materials Science and Engineering, Harbin Institute of Technology, Harbin 150001, China

Abstract:The microstructure evolution of the fine-grained 5083 Al alloy was investigated in annealing temperature range of 150−300 ℃. Then the effects of the different annealed microstructures on high-temperature deformation behavior were further studied. The results indicate that the initial recrystallization temperature is about 200 ℃. By tensile tests at 380−570 ℃ and in strain rate range of 4.17×10−4−1.0×10−2 s−1, the optimum superplastic parameters are obtained as follows: the annealed temperature 250 ℃, the tensile temperature 550 ℃ and the strain rate 4.17×10−4 s−1. With the aid of scanning electronic microscopy (SEM), the fractography of the alloy after the superplastic deformation was analyzed. The results reveal that intergranular cavities with fine size and homogeneous distribution are beneficial to superplastic deformation.

 

Key words: fine-grained 5083 Al alloy; annealing; superplastic deformation

ISSN 1672-7029
CN 43-1423/U

主管:中华人民共和国教育部 主办:中南大学 中国铁道学会 承办:中南大学
湘ICP备09001153号 版权所有:《铁道科学与工程学报》编辑部
------------------------------------------------------------------------------------------
地 址:湖南省长沙市韶山南路22号 邮编:410075
电 话:0731-82655133,82656174   传真:0731-82655133   电子邮箱:jrse@mail.csu.edu.cn