Effect of heat treatment on mechanical properties of thixoformed 7A09 aluminum alloy
WANG Wei-wei(王卫卫), JIA Bin-bin(贾彬彬), LUO Shou-jing(罗守靖)

School of Materials Science and Engineering, Harbin Institute of Technology, Harbin 150001, China

Abstract:The effects of solution-ageing treatment on the mechanical properties of semi-solid metal (SSM) products were studied by the method of orthogonal experiment. The microstructure and tensile properties at different treatment conditions were analyzed. The results show that the effects of solution-ageing treatment were obviously influenced by the original microstructure of the SSM billet. Higher temperature is favorable for the sufficient solution of alloy elements, but the grains will grow up when treated at a higher temperature or soaked for a longer time. There is a contradiction between the maximum tensile strength and elongation percentage. Under the condition of solution treatment at 475 ℃ for 12 h and at 133 ℃ for 20−22 h ageing, better properties including about 540 MPa of tensile strength and more than 6.3% of elongation can be obtained in general. The surplus phases not melted in the substrate and the solution precipitated supersaturated elements are the main factors influencing the properties of the alloys.

 

Key words: 7A09 aluminum alloy; heat treatment; mechanical property; semi-solid metal (SSM)

ISSN 1672-7029
CN 43-1423/U

主管:中华人民共和国教育部 主办:中南大学 中国铁道学会 承办:中南大学
湘ICP备09001153号 版权所有:《铁道科学与工程学报》编辑部
------------------------------------------------------------------------------------------
地 址:湖南省长沙市韶山南路22号 邮编:410075
电 话:0731-82655133,82656174   传真:0731-82655133   电子邮箱:jrse@mail.csu.edu.cn