Fabrication and microstructure of nanostructured Mg-3Ni-2MnO2 by ball milling in hydrogen atmosphere
FANG Wen-bin(房文斌), FANG Wa(房 娃), SUN Hong-fei(孙宏飞), YU Zhen-xing(于振兴)

School of Materials Science and Engineering, Harbin Institute of Technology, Harbin 150001, China

Abstract:Nanostructured Mg-3Ni-2MnO2 was synthesized by ball milling elemental powders of Mg, Ni and MnO2 in hydrogen atmosphere. The microstructures of the powder prepared at different milling time were analyzed by X-ray diffractometry(XRD), scanning electron microscopy(SEM) and high resolution electron microscopy(HREM). The milling time is the most key parameter impacting on the grain size and the microstructure of material. With prolonging the milling time, particle size becomes smaller and smaller. But after the ball milling time reaches about 20 h, reduction of grain size becomes slowly. When the milling time is more than 50 h, nanocrystalline fully forms. When the milling time is more than 80 h, there are more amorphous phases in materials. The average particle diameter of material is about 1 μm and the grain size is 10−30 nm.

 

Key words: nanocrystalline; ball milling; grain size; amorphous phase

ISSN 1672-7029
CN 43-1423/U

主管:中华人民共和国教育部 主办:中南大学 中国铁道学会 承办:中南大学
湘ICP备09001153号 版权所有:《铁道科学与工程学报》编辑部
------------------------------------------------------------------------------------------
地 址:湖南省长沙市韶山南路22号 邮编:410075
电 话:0731-82655133,82656174   传真:0731-82655133   电子邮箱:jrse@mail.csu.edu.cn