Influence of voids on interlaminar shear strength of carbon/epoxy fabric laminates
ZHU Hong-yan(朱洪艳)1, LI Di-hong(李地红)1, ZHANG Dong-xing(张东兴)1,
WU Bao-chang(吴宝昌)2, CHEN Yu-yong(陈玉勇)1

1. School of Materials Science and Engineering, Harbin Institute of Technology, Harbin 150001, China;
2. Harbin Aircraft Industry Co., Ltd., Harbin 150060, China

Abstract:The effects of voids (void content, void shape and size) on the interlaminar shear strength of [(±45)4/(0,90)/(±45)2]S and [(±45)/04/(0,90)/02]S composite laminates were investigated. Specimens with void contents in the range of 0.2%−8.0% for [(±45)4/(0,90)/(±45)2]S and 0.2%−6.1% for [(±45)/04/(0,90)/02]S were fabricated from carbon/epoxy fabric through varying autoclave pressures. The characteristics of the voids were studied by using optical image analysis to explain the interlaminar shear strength results. The influences of voids on the interlaminar shear strength of the two stacking sequences were compared in terms of the void content and size and shape of the void. The effect of voids on the initiation and propagation of interlaminar failure of both stacking sequence composites was found.

 

Key words: carbon fibre reinforced polymer(CFRP) composite; void content; void size; void shape; interlaminar shears strength

ISSN 1672-7029
CN 43-1423/U

主管:中华人民共和国教育部 主办:中南大学 中国铁道学会 承办:中南大学
湘ICP备09001153号 版权所有:《铁道科学与工程学报》编辑部
------------------------------------------------------------------------------------------
地 址:湖南省长沙市韶山南路22号 邮编:410075
电 话:0731-82655133,82656174   传真:0731-82655133   电子邮箱:jrse@mail.csu.edu.cn