Tribological properties of nickel-graphite composite against different counterfaces at elevated temperatures
LI Jian-liang(李建亮), XIONG Dang-sheng(熊党生), WAN Yi(万  轶)

Department of Materials Science and Engineering, Nanjing University of Science and Technology,
Nanjing 210094, China

Abstract:Nickel-based graphite-containing composites were prepared by powder metallurgy method. The effect of graphite addition on mechanical properties of nickel-based alloy was investigated and the tribological properties from room temperature to 600 ℃ were tested by a pin-on-disk tribometer with alumina, silicon nitride and nickel-based alloy as counterfaces. The microstructure was analyzed by X-ray diffraction(XRD) and scanning electron microscope (SEM) attached with energy dispersive spectroscopy(EDS). The worn surfaces at high temperature were observed by optical microscope and SEM. The results show that the tensile strength and hardness of composites decrease after adding graphite, while the friction and wear properties are all improved by adding 12%(mass fraction) graphite. Compared with the counterface of alumina and silicon nitride, the friction coefficients and wear rates are lower when the composite rubs against nickel-based alloy containing molybdenum disulfide.

 

Key words: high-temperature; solid lubrication; self-lubricating composite; Ni-based alloy; graphite

ISSN 1672-7029
CN 43-1423/U

主管:中华人民共和国教育部 主办:中南大学 中国铁道学会 承办:中南大学
湘ICP备09001153号 版权所有:《铁道科学与工程学报》编辑部
------------------------------------------------------------------------------------------
地 址:湖南省长沙市韶山南路22号 邮编:410075
电 话:0731-82655133,82656174   传真:0731-82655133   电子邮箱:jrse@mail.csu.edu.cn