Electrochemical behavior of magnesium alloys in simulated body fluids
ZENG Rong-chang(曾荣昌)1, CHEN Jun(陈  君)1, W. Dietzel2, N. Hort2, K.U. Kainer2

1. School of Materials Science and Engineering, Chongqing Institute of Technology, Chongqing 400050, China;
2. GKSS Research Centre Geesthacht CmbH, Geesthacht 21502, Germany

Abstract:Potentiodynamic electrochemical technique was utilized to study the corrosion behavior of magnesium alloys in simulated body fluids (SBFs). The influence of materials, solutions and their temperature on corrosion rate was mainly discussed. The results demonstrate that the free corrosion potential (Ecorr) of AZ31 and AZ91 alloys rises rapidly at initial stage, and then stabilizes at some value. Ecorr of WE43 alloy increases continuously. While Ecorr of AZ91 alloy with macro-arc oxidation (MAO) coating decreases drastically in 3 min, and then fluctuates between −1 607 mV and −1 503 mV. The WE43 alloy has better corrosion resistance in Hank’s solution, compared with AZ31 and AZ91 alloys. Corrosion rates of the alloys are sensitive to the chemical composition and temperature of SBFs. A thin MgF2 film slightly improves corrosion resistance. An MAO coating on AZ91 alloy significantly reduces corrosion rate and enhances Ecorr. Pitting corrosion occurs on both AZ31 and WE43 alloys in Hank’s solution.

 

Key words: magnesium alloy; biomaterial; corrosion behavior; macro arc oxidation; Hank’s solution

ISSN 1672-7029
CN 43-1423/U

主管:中华人民共和国教育部 主办:中南大学 中国铁道学会 承办:中南大学
湘ICP备09001153号 版权所有:《铁道科学与工程学报》编辑部
------------------------------------------------------------------------------------------
地 址:湖南省长沙市韶山南路22号 邮编:410075
电 话:0731-82655133,82656174   传真:0731-82655133   电子邮箱:jrse@mail.csu.edu.cn