Microstructure characterization and mechanical properties of Mg-9Li-5Al-1Zn-0.6RE alloy
WU Rui-zhi(巫瑞智), ZHANG Mi-lin(张密林), WANG Tao(王 涛)

Key Laboratory of Superlight Materials and Surface Technology, Ministry of Education,
Harbin Engineering University, Harbin 150001, China

Abstract:Mg-9Li-5Al-1Zn-0.6RE alloy was prepared by vacuum induction heating. The microstructure and phases composition of the alloy were analyzed with optical microscope, scanning electron microscope and X-ray diffractometer. Then the effect of homogenization temperature on microstructure and mechanical properties of the alloy was studied. The hardness of samples under different homogenization temperatures was measured. The results show that, the alloy is composed of α phase, β phase, Mg17Al12 and AlLi. RE added into the alloy is solved in α phase and β phase completely. After homogenization heat treatment, the needle-like α phase disappears. With the increase of homogenization temperature, the shape of α phase is spherical-like first, then vermicular-like, and large block-like finally. The variation of the shape of α phase causes the hardness of sample to change accordingly. The most favorable homogenization temperature for microstructure and mechanical properties is 150 ℃.

 

Key words: homogenization temperature; magnesium-lithium alloy; microstructure; mechanical properties

ISSN 1672-7029
CN 43-1423/U

主管:中华人民共和国教育部 主办:中南大学 中国铁道学会 承办:中南大学
湘ICP备09001153号 版权所有:《铁道科学与工程学报》编辑部
------------------------------------------------------------------------------------------
地 址:湖南省长沙市韶山南路22号 邮编:410075
电 话:0731-82655133,82656174   传真:0731-82655133   电子邮箱:jrse@mail.csu.edu.cn