Tensile and creep properties of Ti-600 alloy
ZENG Li-ying(曾立英)1, 2, HONG Quan(洪  权)1, YANG Guan-jun(杨冠军)2,
ZHAO Yong-qing(赵永庆)1, QI Yun-lian(戚运莲)1, GUO Ping(郭 

1. Northwest Institute for Nonferrous Metal Research, Xi’an 710016, China;
2. School of Metallurgical Engineering, Xi’an University of Architecture and Technology, Xi’an 710055, China

Abstract:Ti-600 is one of the high performance titanium alloys used at 600 ℃, which was developed in Northwest Institute for Nonferrous Metal Research (NIN) in China. The tensile and creep properties of Ti-600 alloy with different thermal treatment conditions were investigated. The results indicate that Ti-600 alloy possesses favorite comprehensive properties solution-treated at  1 020 ℃ for 1 h, then air-cool, and aged at 650 ℃ for 8 h, finally air-cooling, especially possesses quite good creep resistance. The residual deformation is less than 0.1% for the alloy exposed at 600 ℃ for 100 h with the stress of 150 MPa, and the bimodal microstructures of the alloy are almost the same as that of the alloy treated by duplex thermal treatment, only needle primary a phases became relatively thicker and coarsened. The ultimate strength and the elongation of the alloy tested at ambient temperature are 1 080 MPa and 12%, respectively; while at 600 ℃, they are 690 MPa and 16%, respectively. The ductility of the alloy tested at room, temperature is no less than 5% after thermal exposing at 600 ℃ for 100 h.

 

Key words: Ti-600 alloy; high temperature titanium alloy; tensile property; creep resistance

ISSN 1672-7029
CN 43-1423/U

主管:中华人民共和国教育部 主办:中南大学 中国铁道学会 承办:中南大学
湘ICP备09001153号 版权所有:《铁道科学与工程学报》编辑部
------------------------------------------------------------------------------------------
地 址:湖南省长沙市韶山南路22号 邮编:410075
电 话:0731-82655133,82656174   传真:0731-82655133   电子邮箱:jrse@mail.csu.edu.cn