Hot deformation and processing maps of titanium matrix composite
WANG Rui-ning(王蕊宁)1, 2, XI Zheng-ping(奚正平)2, ZHAO Yong-qing(赵永庆)2,
QI Yun-lian(戚运莲)2

1. School of Materials Science and Engineering, Xi’an University of Architectural and Technology,
Xi’an 710055, China;
2. Titanium Research Center, Northwest Institute for Nonferrous Metal Research, Xi’an 710016, China

Abstract:The hot deformation characteristics of TiC particles reinforced titanium matrix composite were studied in the temperature range from 900 ℃ to 1 150 ℃ and in the strain rate range of 10−3−10 s−1 by compression tests with Gleeble1500 simulator system. The flow behavior was described by the hyperbolic sine constitutive equation, and an average activation energy of 436.72 kJ/mol was calculated. The processing maps were calculated and analyzed according to the dynamic materials model. The maps show domains in some combinations of temperatures and strain rates and these domains are correlated with specific microstructural processes occurring during hot deformation by metallographic investigations and kinetic analysis. At the low strain rate domain occurs in the temperature range of 900−960 ℃ and strain rate range of 0.001−0.03 s−1 superplasticity and dynamic recrystallization were observed. At a high strain rate domain occurs in the temperature range of 980−1 120 ℃ and strain rate range of 0.1−10 s−1 the β phase undergoes dynamic recrystallization. Also, at a strain rate range of 0.1−10 s−1 and the temperature range of 900−930 ℃, the material exhibits flow localization.

 

Key words: titanium matrix composite; hot deformation; processing map

ISSN 1672-7029
CN 43-1423/U

主管:中华人民共和国教育部 主办:中南大学 中国铁道学会 承办:中南大学
湘ICP备09001153号 版权所有:《铁道科学与工程学报》编辑部
------------------------------------------------------------------------------------------
地 址:湖南省长沙市韶山南路22号 邮编:410075
电 话:0731-82655133,82656174   传真:0731-82655133   电子邮箱:jrse@mail.csu.edu.cn