EXPERIMENTAL SIMULATION ON CONTROL ROLLING PROCESS OF6201ALUMINUM ALLOY
Liu Yuying, Zhang Hui, Peng Dashu, Wang Caikun

Department of Materials Science and Engineering,Central South University of Technology, Changsha 410083 P. R. China

Abstract:Control rolling process of 6201 aluminum alloy was simulated on Gleeble-1500. The deformed specimens under different processes were analyzed by the observation of optical microscopy and TEM, and the measurement of hardness. It was shown that solid solution and aging treatment can be effectively combined in one procedure by control rolling process, the deformation temperature is ranging from 540℃to 200℃. Precipitation of Mg2Si is accelerated by the rising of the finishing temperature, the amount of precipitates increases with holding time after deformation. A more uniformly distributed and finer Mg2Si particles can be observed on deformed specimens which have been subsequently held at 250~300℃for 60s.

 

Key words: 6201 aluminum alloy control rolling process thermal simulation Mg2Si precipitation

ISSN 1672-7029
CN 43-1423/U

主管:中华人民共和国教育部 主办:中南大学 中国铁道学会 承办:中南大学
湘ICP备09001153号 版权所有:《铁道科学与工程学报》编辑部
------------------------------------------------------------------------------------------
地 址:湖南省长沙市韶山南路22号 邮编:410075
电 话:0731-82655133,82656174   传真:0731-82655133   电子邮箱:jrse@mail.csu.edu.cn