Diffusion bonding mechanism and microstructure ofwelded joint of aluminium matrix composite Al2O3p,/6061
Liu Liming(刘黎明); Niu Jitai(牛济泰); Tian Yanhong (田艳红); Meng Xiaodong(孟晓东)

National Key Laboratory of Advanced Welding Production Technology; Harbin Institute of Technology; Harbin 150001; P. R. China;
General Chnsulate of Sweden in Shanghai; Shanghai 200031; P. R. China

Abstract:Relationships between microstructures of welded joint and welding parameters or weld strength of aluminium matrix composite Al2O3p/6061 subjected to diffusion welding were studied. The results are as follows: key factor affecting strength of welded joint is oxide in the weld zone. The existence of oxide in the welded joint not only hinders the diffusion of the matrix atoms, but also destroys the good interface between the matrix and the reinforced phase. The oxides turn into fine particles from film with increasing welding temperature, and the destroying effect on welded joint decreases, which increases the strength of the welded joint. On the basis of this, the diffusion welding of aluminium matrix composite Al2O3p/6061 was successfully

 

Key words:  aluminium matrix composite; oxide; welded joints; microstructure

ISSN 1672-7029
CN 43-1423/U

主管:中华人民共和国教育部 主办:中南大学 中国铁道学会 承办:中南大学
湘ICP备09001153号 版权所有:《铁道科学与工程学报》编辑部
------------------------------------------------------------------------------------------
地 址:湖南省长沙市韶山南路22号 邮编:410075
电 话:0731-82655133,82656174   传真:0731-82655133   电子邮箱:jrse@mail.csu.edu.cn