SOLIDIFICATION AND MICROSEGREGATION BEHAVIORS OF NICKEL-BASE SINGLE CRYSTAL SUPERALLOY SOLIDIFIED AT MEDIUM COOLING RATE
Du Wei, Li Jianguo and Fu Hengzhi

State Key Laboratory of Solidification Processing,Northwestern Polytechnical University, Xi′an 710072, P. R. China

Abstract:Single crystal blades have already been used in some advanced engines. An industrially valuable nickel-base single crystal superalloy CMSX-2 was solidified at cooling rate from below 1 K/s to 20 K/s. Microstructure and microsegregation were investigated. The results showed that the dendritic arm spacing is highly refined at high cooling rate, the primary dendritic arm spacing can be 35μm, just as 1/10 as that by conventional HRS processing. With the increase of cooling rate, the microsegregation increases and then decreases. In the superfine columnar dendrite, theγ′precipitates are very fine; the amount ofγ/γ′eutectic is much fewer and its size is very small.

 

Key words: single crystal superalloy cooling rate microstructure microsegregation

ISSN 1672-7029
CN 43-1423/U

主管:中华人民共和国教育部 主办:中南大学 中国铁道学会 承办:中南大学
湘ICP备09001153号 版权所有:《铁道科学与工程学报》编辑部
------------------------------------------------------------------------------------------
地 址:湖南省长沙市韶山南路22号 邮编:410075
电 话:0731-82655133,82656174   传真:0731-82655133   电子邮箱:jrse@mail.csu.edu.cn